Polypropylene fibrillated fibers PPF
Dosage
The dosage of PPF FIBROMIX is of 0,9 kg per cubic meter of concrete; in case of particular applications don’t hesitate to contact our technical service.
Application
PPF FIBROMIX fibers can be used with all types of concrete, mixture they improve the characteristics of the waterproof, durability, abrasions and cracks resistance.
Ideal for:
- Industrial floors
- Pavements
- Garage floors
- Kerb stone
- Marine and water structures
- Sprayed concrete
- Walls
- Hand manufactured concrete
Advice for use:
| mm 19 | concrete/industrial floors |
| mm 19/25/31/38 | pumped concrete and inclined casting |
| mm 19/25 | concrete tubes |
Polypropylene monofilaments fibers PPM
Dosage
The dosage of PPM FIBROMIX is of 140 kg for every mixture made by 25 kg of concrete; in case of particular applications don’t hesitate to contact our technical service.
Application
PPM FIBROMIX fibers can be used with all types of concrete, mixture they improve the characteristics of the waterproof, durability, abrasions and cracks resistance.
Ideal for:
- Outside and inside plasters
- Pre-mixed plasters
- Coverings
- Prefabricated elements
- Walls
- Mortars
- Plasters
- Stucco works
- Low thickness sections
- Restoration works
Consigli d’uso:
| mm 6/9 | plaster/pre-mixing plaster |
| mm 3/6/9/12 | plasters |
| mm 6/9/12 | repair mortar |
| mm 9/12 | precast concrete elements |
PRODUCTS - edilizia - Fibromix
FIBROMIX are 100% virgin-polypropylene fibers without reprocessed olefin materials, produced in according to our certification SGS ISO 9000:2000 and specifications ASTM 1116 TYPE III GMP specially studied for concrete industry
- Increases impact, abrasion and shatter resistance in concrete
- Reduces the concrete cracking as a result of intrinsic stresses
- Produce a micro-reinforcement system making a more cohesive mixture
- 5 minutes mixing time is enough for proper distribution
- Sono chimicamente inerti, quindi non reagiscono a nessun tipo di additivo e/o prodotto chimico eventualmente aggiunto al calcestruzzo
- Non hanno nessuna reazione negli ambienti alcalini del calcestruzzo
- Very easy to use, FIBROMIOX an be added into the standard concrete mixture
- Chemically inert and do not after performance of the concrete additives
- Anti-alkali resistant
- Increase resistance to abrasion, shatters, impacts and thermal shocks
- Increase long-term durability of the concrete by improving the impermeability and retarding corrosion of the metal
- reinforcement system
- Accelerate a lot the production time
Polypropylene fibrillated fibers PPF
| Caratteristiche chimico / fisiche Chemical and physical characteristics |
|
| Lunghezza fibre mm Fibers lenght mm |
3/6/9/12/15/19/21/25/31/38/46/51 |
| Peso specifico Specific weight |
0.91 |
| Punto di accensione Ignition point |
+ 590 °C |
| Punto di fusione Melting |
+ 160 °C |
| Assorbimento acqua Water absorption |
nullo nil |
| Conduttività termica Thermal conducivity |
bassa low |
| Resistenza agli acidi Acid resistance |
alta high |
| Resistenza ai Sali Salt resistance |
alta high |
| Resistenza agli alcali Alcaline resistance |
alta high |
| Conduttività termica Electric conducivity |
bassa low |
| Resistenza alla trazione Tensil strenght |
400 N/mm2 |
| Allungamento Elongation |
15% |
| Modulo elastico di YOUNG YOUNG’S elastic module |
R/A = 400/0,15 = 2666 N/mm2 = 266 kg/mm2 |
| Sezione trasversale Cross section |
0,31 mm2 |
Polypropylene monofilaments fibers PPM
| Caratteristiche chimico / fisiche Chemical and physical characteristics |
|
| Lunghezza fibre mm Fibers lenght mm |
3/6/9/12/15/19/21/25/31/38/46/51 |
| Peso specifico Specific weight |
0.91 |
| Punto di accensione Ignition point |
+ 590 °C |
| Punto di fusione Melting |
+ 160 °C |
| Assorbimento acqua Water absorption |
nullo nil |
| Conduttività termica Thermal conducivity |
bassa low |
| Resistenza agli acidi Acid resistance |
alta high |
| Resistenza ai Sali Salt resistance |
alta high |
| Resistenza agli alcali Alcaline resistance |
alta high |
| Conduttività termica Electric conducivity |
bassa low |
| Resistenza alla trazione Tensil strenght |
700 N/mm2 |
| Allungamento Elongation |
15% |
| Modulo elastico di YOUNG YOUNG’S elastic module |
R/A = 700/0,15 = 4666 N/mm2 = 466 kg/mm2 |
| Sezione trasversale Cross section |
0,24 mm2 |